ADK CYCLOAID PNB Series ― Polymeric Plasticizers for environment-friendly PVC

ADK CYCLOAID PNB Series produced from biomass materials that are well-suited to a sustainability-oriented society. Compared to general-purpose plasticizers such as phthalates or dibasic esters, PNB Series exhibit equal or better performance in terms of oil resistance (resistance to oil extraction), heat aging stability, and less-migration to other plastics.

ADK CYCLOAID PNB-205

This plasticizer uses 90% or more biomass raw materials.
* Currently in the process of acquiring the Biomass Mark certification from the Japan Organics.
* This product will be launched in Japan, targeted to be worldwide in the future.

Data of ADK CYCLOAID PNB-205

PNB-205

DOP

DOTP

Epoxy type

Polyester type

Viscosity (mPa・s/25℃)

mPa・s

500

60

60

380

500

Color tone stability

180℃×5min, 2mm

Y.I

14.0

11.7

13.1

15.7

12.3

Transparency

180℃×5min, 2mm

Haze

2.6

1.9

2.1

2.3

2.9

Electrical insulating

Volume intrinsic resistance
(30℃, 500V)

Ω・cm

1.0
x
1011

10.0
x
1011

16.8
x
1011

4.9
x
1011

1.1
x
1011

Cold resistance

Clash-Berg (Tf)

-20.1

-25.8

-26.7

-14.3

-14.0

Migration test

ABS (70℃)

*

±

--

--

±

±

Tensil testing

Tensil strength

MPa

22.6

20.1

22.2

22.2

22.5

100% modulus

MPa

12.0

10.6

11.2

11.4

11.7

Elongation

%

360

350

350

340

320

Heat aging stability 100℃×120h

Volatile loss

%

1.2

3.0

1.1

0.3

1.2

Elongation retention

%

98

92

95

99

97

Oil resistance 100℃×96h ASTM No.2 oil

Extracted volume

%

11.4

16.2

15.0

11.0

11.4

Compatibility 40℃×80%RH×4 weeks

Bleeding

*

++

* ++: Excellent, +: Good, -: Average, --: Poor
Composition:PVC(p=1,050)100 / Stabilizer (Ba-Zn) 2.5 / Plasticizer 50

Applications

PVC Film, Sheet, and daily-use industrial products, etc.